Kiiltomelt S 310 beige
Hot melt adhesive
Kiiltomelt S 310 is an unfilled EVAC-based hot melt adhesive for edge banding.
Special features
- M1 classification
Links
Materials
Kiiltomelt S 310 is an unfilled edge banding hot melt adhesive which provides a thin and invisible joint. Suitable for melamine impregnated paper edge strips, PVC-edge strips/laths, ABS-edge strips/laths, veneer strips, laminate and solid wood laths gluing. Adhesive is compliant with Finnish Emission Classification of Building Materials (M1).
| Package Size | Product Code |
|---|---|
| Kiiltomelt S 310 beige 10 kg | T7307.010 |
13%
beige
106 °C (DIN 52011)
54 000 mPas, 200 °C, 3 s¯¹
+18–22 °C
200 - 210 °C (application roller)
10 kg
60 - 70 %
7 - 10 %
In unopened containers, at max. +40 °C, for 36 months.
The adhesive is melted in the adhesive tank. The minimum feed speed of the machine is 18 m/min. If the feed speed is lower than recommended, the adhesive temperature on the applicator roll must be raised in order to avoid the adhesive from cooling prematurely. For longer breaks in the work the adhesive temperature should be decreased, because otherwise the adhesion and flowing properties of the adhesive may weaken.
The information given in this product data sheet is based on our tests and our practical knowledge. The technical data is defined in standard conditions. Variations in local working conditions will affect the product performance and result. The result is also strongly affected by working methods. We guarantee the high quality of our products according to our Quality Management System. No liability can be accepted from incorrect use of the product or prevailing conditions, over which we have no control. Thus, we cannot be held responsible for the final result. The user of the product must test product’s suitability to the intended application.